Sikadur®-30 LP
Sikadur®-30 LP is a thixotropic, structural 2-component adhesive, based on a combination of epoxy resins and especially designed for use at higher temperatures between +25 °C and +55 °C.
- Long pot life
- High temperature resistance at elevated curing temperatures
- Easy to mix and apply
- No primer needed
- High creep resistance under permanent load
- Very good adhesion to concrete, masonry, stonework, steel, cast iron, aluminium, timber and Sika® CarboDur® Plates
- Hardening is not affected by high humidity
- High strength adhesive
- Thixotropic: non-sag in vertical and overhead applications
- Hardens without shrinkage
- Different coloured components (for mixing control)
- High initial and ultimate mechanical resistance
- High abrasion and shock resistance
- Impermeable to liquids and water vapour
Usage
Adhesive for bonding structural reinforcement, particularly in structural strengthening works. Especially for the following uses:- Sika® CarboDur® Plates to concrete, brickwork, timber and steel (for details see the Sika® CarboDur® Product Data Sheet, the “Method Statement for Sika® CarboDur® Externally Bonded Reinforcement” Ref: 850 41 05 and the “Method Statement for Sika® CarboDur® Near Surface Mounted Reinforcement” Ref: 850 41 07).
- Steel plates to concrete (for details see the relevant Sika Technical information).
Advantages
Sikadur®-30 LP has the following advantages:- Long pot life
- High temperature resistance at elevated curing temperatures
- Easy to mix and apply
- No primer needed
- High creep resistance under permanent load
- Very good adhesion to concrete, masonry, stonework, steel, cast iron, aluminium, timber and Sika® CarboDur® Plates
- Hardening is not affected by high humidity
- High strength adhesive
- Thixotropic: non-sag in vertical and overhead applications
- Hardens without shrinkage
- Different coloured components (for mixing control)
- High initial and ultimate mechanical resistance
- High abrasion and shock resistance
- Impermeable to liquids and water vapour
Packaging
6 kg (A+B) | Pre-batched unit |
pallets of 480 kg (80 x 6 kg) |
Colour
Component A: white
Component B: black
Component A + B mixed: light grey
Product Details
APPROVALS / CERTIFICATES
- Structural bonding product for bonded plate reinforcement according to EN 1504-4:2004, Declaration of Performance 0202060400100000031001, certified by notified factory production control certification body 0921, certificate of conformity of the factory production control 0921-CPR-2054, and provided with the CE marking.
Composition
Epoxy resin
Shelf life
24 months from date of production
Storage conditions
Store in original, unopened, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight.
Density
1.65 kg/l ±0.1 kg/l (components A+B mixed) (at +23 °C) |
System structure
Sika® CarboDur® System: For Application Details of Sika® CarboDur® plates with Sikadur®-30 LP, see the “Method Statement for Sika® CarboDur® Externally Bonded Reinforcement” Ref: 850 41 05 and the “Method Statement for Sika® CarboDur® Near Surface Mounted Reinforcement” Ref: 850 41 07
Compressive strength
Curing time | Curing temperature | |
+25 °C | +55 °C | |
12 hours | − | ~90 N/mm2 |
1 day | ~75 N/mm2 | ~100 N/mm2 |
3 days | ~85 N/mm2 | ~110 N/mm2 |
Modulus of elasticity in compression
~10 000 N/mm2 (at +25 °C) | (ASTM D 695) |
Tensile strength in flexure
Curing time | Curing temperature | |
+25 °C | +55 °C | |
1 day | ~12 N/mm2 | ~38 N/mm2 |
3 days | ~20 N/mm2 | ~40 N/mm2 |
7 days | ~25 N/mm2 | ~42 N/mm2 |
Tensile strength
Curing time | Curing temperature | |
+25 °C | +55 °C | |
1 day | − | ~26 N/mm2 |
3 days | ~14 N/mm2 | ~28 N/mm2 |
7 days | ~17 N/mm2 | ~28 N/mm2 |
Tensile adhesion strength
Curing time | Substrate Curing temperature | ||
+25 °C | +55 °C | ||
1 day | Concrete | >4 N/mm2 (Concrete fracture) | >4 N/mm2 (Concrete fracture) |
1 day | Steel | 15 N/mm2 | 25 N/mm2 |
3 days | Steel | 22 N/mm2 | 28 N/mm2 |
Shear strength
Curing time | Curing temperature | ||
+25 °C | +44−55 °C | +80 °C | |
>1 hour | − | − | *17 N/mm2 |
7 days | *7 N/mm2 | ~19 N/mm2 | − |
*(DIN EN 1465)
Shrinkage
0.04 % | (FIP: Fédération Internationale de la Précontrainte) |
Coefficient of thermal expansion
2.5 x 10−5 1/K (Temperature range: −20 °C to +40 °C) | (EN 1770) |
Glass transition temperature
Curing time | Curing temperature | TG |
3 days / 1 day | +23°C / +80 °C | +90 °C |
3 days / 1 day | +23°C / +50 °C | +80 °C |
30 days | +30 °C | +70 °C |
Heat deflection temperature
Curing time | Curing temperature | HDT |
2 hours | +80 °C | +84 °C |
7 days | +55 °C | +82 °C |
7 days | +23 °C | +55 °C |
Service temperature
−40 °C to +45 °C (when cured at > +23 °C)
−40 °C to +72 °C (when cured > 2 hours at +80 °C within 7 days)
Application
Mixing ratio
Component A : Component B = 3 : 1 by weight or volume
Only mix complete pre-batched units of Sikadur®-30 LP.
Layer thickness
30 mm max.
Sag flow
On vertical surfaces it is non-sag up to 3−5 mm thickness at +55 °C. | (FIP: Fédération Internationale de la Précontrainte) |
Squeezability
5 500 mm2 at +25 °C at 15 kg | (FIP: Fédération Internationale de la Précontrainte) |
Product temperature
Sikadur®-30 LP must be applied at temperatures between +20 °C and +40 °C.
Ambient air temperature
+25 °C min. / +55 °C max.
Dew point
Beware of condensation.
Substrate temperature during application must be at least 3 °C above dew point.
Substrate temperature
+25 °C min. / +55 °C max.
Substrate moisture content
Max. 4 % pbw
When applied to mat damp concrete, brush the adhesive well into the substrate.
Pot Life
Temperature | Potlife | Open time |
+25 °C | ~90 minutes | ~120 minutes |
+55 °C | ~30 minutes | ~60 minutes |
The potlife begins when the resin and hardener are mixed. It is shorter at high temperatures and longer at low temperatures. The greater the quantity mixed, the shorter the potlife. To obtain longer workability at high temperatures, the mixed adhesive may be divided into portions. Another method is to chill components A+B before mixing them (not below +5 °C).
SUBSTRATE QUALITY
See the Product Data Sheet of Sika® CarboDur® Plates and Sika® CarboDur® BC rods.
SUBSTRATE PREPARATION
See the “Method Statement for Sika CarboDur® Externally Bonded Reinforcement” Ref: 850 41 05 and the “Method Statement for Sika CarboDur® Near Surface Mounted Reinforcement” Ref: 850 41 07.
MIXING
Pre-batched units:
Mix components A+B together for at least 3 minutes with a mixing spindle attached to a slow speed electric drill (max. 300 rpm) until the material becomes smooth in consistency and a uniform grey colour. Avoid aeration while mixing. Then, pour the whole mix into a clean container and stir again for approx. 1 more minute at low speed to keep air entrapment at a minimum. Mix only that quantity which can be used within its potlife.
CLEANING OF EQUIPMENT
Clean all tools and application equipment with Sika® Colma Cleaner immediately after use. Hardened / cured material can only be mechanically removed.