Sikagard®-403 W
Sikagard®-403 W is a single component, waterborne modified acrylic resin based intermediate and surface coating, containing an antimicrobial additive.
- Seamless, easy to clean finish
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good water vapour permeability
- More flexible in comparison to standard acrylic paints, improves resistance to cracking and flaking
- Ultra-low emissions
- Good opacity
- Odourless
- Easy to apply
Usage
- Application on concrete, bricks, cement and gypsum based substrates, metal surfaces, timber, tiles and plastic
- Embedment, intermediate and top coat for internal walls and ceilings
- Suitable for production facilities in the pharmaceutical, medical engineering, food and beverage industry, as well as, hospitals, prisons, healthcare and leisure facilities
Advantages
- Seamless, easy to clean finish
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good water vapour permeability
- More flexible in comparison to standard acrylic paints, improves resistance to cracking and flaking
- Ultra-low emissions
- Good opacity
- Odourless
- Easy to apply
Packaging
5.0 l = 6.60 kg drums
15.0 l = 19.80 kg drums
Colour
white
pastel colour shades on request
Product Details
SUSTAINABILITY
Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings
APPROVALS / CERTIFICATES
- Eurofins, test report No. 392-2014-0027 0301, VOC emission acc. French Regulations Decret DEVL 11019093D, March 23, 2011 and Decret DEVL 11034675A, February 15, 2016.
- PRA, test report No. 77388-004, gloss, fineness, grind wet scrub resistance and contrast ratio according to EN 13300, September 30, 2014.
- Exova Warrigtonfire, test report No. WF 343711, classification reaction to fire according to EN 13501-1:2007+A1:2009, September 15, 2014.
- IMSL, test report No. 2014/02/011.1A-1, determination of antibacterial activity according to ISO 22196, December 29th 2014.
- IMSL, test report No. 2014/12/009.2A, determination of resistance of surface coatings to mould growth according to BS 3900, Part G6, April 21, 2015
- 4wardtesting, test report No. C2882, water vapour transmission rate and water vapour permeability according to ISO 7783-1:2000 (superseded by EN ISO 7783:2011, November 30, 2011), August 29, 2014.
- Eurofins, test report No. 392-2015-00292201, determination of VOC and SVOC content according ISO 11890-2, CEPE/EC/2015-04-13 and Commission Decision 2014/312/EU, October 6, 2015
- KIWA GmbH Polymer Institute, test report P10108-E, determination of crack bridging properties according to DIN EN 1062-7, April 12, 2016
- Campden BRI Group, test report No. S/REP/139540/1Sensory Evaluation of the Taint Potential, Triangle Test Method TES -S-002, Odour Transfer Method, July 15, 2016
Composition
Styrene-acrylic copolymer dispersion, waterborne
Shelf life
12 months from date of production
Storage conditions
Store in closed, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight and frost.
Density
~1.34 kg/l (+23 °C) | (EN ISO 2811-1) |
Solid content by weight
~61 %
Solid content by volume
~47 %
Tensile strength
~2.8 N/mm² unreinforced | (EN ISO 527-3) |
Tensile adhesion strength
> 1.5 N/mm² to concrete primed with Sika Bonding Primer | (ISO 4624) |
Chemical resistance
Resistant to mild detergents and cleaning agents. Please contact Sika technical service for specific information.
Disinfection with Hydrogen Peroxide Vapour:
- Resistant when using Steris VHP technology
- Resistant to PEA vaporisation technology, when a system build up with glass fibre reinforcement is used
- Resistant when using Oxypharm vaporiser type NOCOSPRAY under following conditions:
Disinfectant | Concentration | Setting at vaporiser | Contact time |
NOCOLYSE Mint (6 %) | 1 ml/m³ | 20 m³ | 30 min |
NOCOLYSE One Shot (12 %) | 3 ml/m³ | 45m³ | 30 min |
NOCOLYSE Food (7.9 %) | 1 ml/m³ | 20 m³ | 30 min |
NOCOLYSE Food (7.9 %) | 5 ml/m³ (2 cycles) | 75m³ (5 minutes vaporisation) | 60 min |
Permeability to water vapour
~37.5 g/m² in 24 hours | (EN ISO 7783-1) |
Application
Layer thickness
Wet film thickness | ~200 µm per layer unreinforced |
Dry film thickness | ~100 µm per layer unreinforced |
Product temperature
+8 °C min. / +35 °C max.
Ambient air temperature
+8 °C min. / +35 °C max.
Relative air humidity
< 80 %
Dew point
Beware of condenstation
Substrate temperature must be at least +3 °C above dew point
Substrate temperature
+8 °C min. / +35 °C max.
Substrate moisture content
Visible damp free
Curing time
Before overcoating with Sikagard®-403 W
Temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 2 hours | 7 days |
+30 °C | 1 hour | 7 days |
Before overcoating with 2-comonent top coats
Temperature | Minimum | Maximum |
+10 °C | 16 hours | 7 days |
+20 °C | 8 hours | 7 days |
+30 °C | 4 hours | 7 days |
Consumption
~0.28 kg/m² per layer unreinforced
~0.80 kg/m² per layer for reinforcement with Sika Reemat Premium
APPLICATION
Stir product mechanically until a uniform liquid has been achieved.
Use a low speed electrical stirrer (300-400 rpm) to avoid air entrapment.
For roller application use short piled roller.
For airless application use tip sizes from 0.38 to 0.53 mm and angle from 40° to 60°.
CLEANING OF EQUIPMENT
Clean all tools with water immediately after use. Hardened and/or cured material can only be removed mechanically.