Product Data Sheet Show all documents

Sikalastic®-851 R

Two-component spray applied roof waterproofing membrane

Sikalastic®-851 R is a two component, elastic, crack-bridging, rapid-curing modified polyurethane/ polyurea-hybrid membrane. Sikalastic®-851 R is applied by two compontent hot spray equipment.

  • Solvent free
  • Fast application - application with 2-part hot spray equipment
  • Fast curing - over coating with top coat possible after approx. 10 minutes
  • Seamless waterproofing membrane
  • High Solids - contains no fillers
 
  • Excellent crack-bridging properties
  • Highly elastic and crack bridging
  • Low viscosity
  • Water vapour permeable – allows the substrate to breathe
  • Good adhesion to most substrates
  • 12 months shelf life
Product Data Sheet Show all documents

Usage

  • For use as a waterproofing membrane on flat and pitched roof structures with additional top coat for UV-protection for exposed roofs.
  • For use as a waterproofing membrane underneath planting or hard landscaping on podium areas.
  • For use as a waterproofing membrane for other concrete structures and on non-trafficked concrete areas with an additional top coat for UV-protection.

Advantages

  • Solvent free
  • Fast application - application with 2-part hot spray equipment
  • Fast curing - over coating with top coat possible after approx. 10 minutes
  • Seamless waterproofing membrane
  • High Solids - contains no fillers
 
  • Excellent crack-bridging properties
  • Highly elastic and crack bridging
  • Low viscosity
  • Water vapour permeable – allows the substrate to breathe
  • Good adhesion to most substrates
  • 12 months shelf life

Packaging

Component A

211 kg drum

Component B

202 kg drum

Colour

Component A (ISO)

clear / brownish

Component B (Resin)

grey or yellowish

Mixed product: grey ~ca. RAL 7004

Product Details

Sustainability / Certifications / Approvals

SUSTAINABILITY

Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings

APPROVALS / CERTIFICATES

  • Test report for root resistance following DIN 4062: report No.: P9638-1-E dated 29/05/2015
  • Test report for crack bridging properties following DIN EN 1062-7: report No.: P 9638-2-E dated 29/05/2015
  • Test report for fire classification according to EN 13501-1, following test method DIN EN ISO 11925-2,: report No. 903 0526000-2 dated 15/8/2015; reaction to fire performance: class E
 
Product Information

Composition

Modified Polyurethane/ Polyurea-Hybrid

Shelf life

Component A

12 months from date of production

Component B

12 months from date of production

Storage conditions

The product must be stored properly in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C.
Higher storage temperatures may reduce shelf life of product.
Reference shall also be made to the storage recommendations within the safety data sheet.

Density

Component A

~1,08 kg/l

Component B

~1,04 kg/l

Mixed resin

~1,00 kg/l (cured film)

All density values at +23 °C

Solid content

> 99 %

Viscosity

Component A

~2300 mPa·s at +20 °C

Component B

~2300 mPa·s at +20 °C
System information

System structure

Exposed Roof Waterproofing

Sikalastic®-851 R is applied in one coat and sealed with one coat Sikalastic®-621 or Sikalastic®-445

Layer

Product

Consumption

1. Primerplease refer to substrate pre-treatmentplease refer to PDS of the primer

2. Waterproofing

Sikalastic®-851 R≥ 1,6 kg/m2

3. UV Protection

Sikalastic®-621 or Sikalastic®-445≥ 1,0 kg/m2

Non-Exposed Roof Waterproofing

Sikalastic®-851 R is applied in one or two coats

Layer

ProductConsumption
1. Primerplease refer to substrate pre-treatmentplease refer to PDS of the primer
2. WaterproofingSikalastic®-851 R≥ 2,1 kg/m2

 Note: These figures are theoretical and do not include for any additional material required due to surface porosity, surface profile, variations in level and wastage.
Technical Information

Shore A hardness

TemperatureAfter 1 hour

After 24 hours

After 28 days

+8 °C

~81

~88

~88

+23 °C

~83

~88

~88

Tensile strength

~11,0 N/mm2 (28 days / +23 °C)

(DIN 53504)

Crack bridging ability

Dynamic crack-bridging class

B 4.2

Static crack-bridging class

A 5

Resistance to root penetration

free of penetration of the roots
free of growth into the ground

(DIN 4062)

Reaction to fire

Euroclass E

(EN 13501-1; DIN  EN ISO 11925-2 )

Chemical resistance

Sikalastic®-851 R is generally resistant to:

  • Bitumen
  • Alkalis

Temperature resistance

Sikalastic®-851 R is short term resistant to mastic asphalt (hot poured asphalt) applied at a max. of +240 °C.

Sikalastic®-851 R elastic properties are maintained at temperatures as low as -30 °C.

 

Dry film thickness

Exposed Roof Waterproofing

Waterproofing~1,6 mm
UV Protection~0,5 mm
Total~2,0 mm

Non-Exposed Roof Waterproofing

Waterproofing~2,1 mm

Application

Application Information

Mixing ratio

Component A : Component B = 1 : 1 (by volume)

Component A : Component B = 1,04 : 1 (by weight)

Product temperature

Component A

+70–80 °C

Component B

+65–70 °C

Hose

+65–70 °C

Ambient air temperature

+8 °C min. / +50 °C max.

Relative air humidity

80 % r.h. max

Substrate temperature

+8 °C min. / +55 °C max.

≥3 °C above dew point

Substrate moisture content

≤ 4 % pbw moisture content.
Test method: Sika®-Tramex meter, CM - measurement on Oven-dry method
No rising moisture according to ASTM (Polyethylene-sheet).

Substrate pre-treatment

Substrate

Primer

Cementitious substrates

Sika® Concrete Primer or Sikafloor®-161 lightly broadcast with quartz sand, 0,3–0,8 mm

Ceramic tiles (unglazed), and concrete slabs

Sika® Concrete Primer

Bituminous feltSikalastic® Metal Primer
Bituminous coatingsSikalastic® Metal Primer

Metals

Ferrous or galvanised metals, lead, copper,aluminium, brass or stainless steel

Sikalastic® Metal Primer

For the consumption rates and waiting time / overcoating please refer to the PDS of the appropriate primer. Other substrates must be tested for their compatibility. If in doubt, apply a test area first.

Waiting time to overcoating

Before applying Sikalastic®-851 R on Sikafloor®-161 allow:

Substrate temperature

Minimum waiting time

Maximum waiting time1

+10 °C

24 hours

1 month

+20 °C

12 hours

1 month

+30 °C

8 hours

1 month

+45 °C6 hours1 month

Before applying Sikalastic®-851 R on Sikalastic®-851 R allow:

Substrate temperature

Minimum waiting time

Maximum waiting time2

+10 °C

4 minutes

3 hours

+20 °C

4 minutes

3 hours

+30 °C

4 minutes

1 hour

+45 °C4 minutes1 hour

Before applying Sikalastic®-621 or Sikalastic®-445 on Sikalastic®-851 R allow:

Substrate temperature

Minimum waiting time

Maximum waiting time2

+10 °C

10 minutes

24 hours

+20 °C

10 minutes

24 hours

+30 °C

10 minutes

24 hours

+45 °C10 minutes24 hours

1 Assuming that any dirt has been carefully removed and any contamination is avoided.

2 If the maximum waiting time is exceeded, Sika® Concrete Primer has to be applied with a consumption rate of 100 g/m2 as an adhesion promoter between the layers.
 

 Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Applied product ready for use

Rain resistant after

Ready for foot traffic1 (careful)

Ready for foot traffic

Ambient conditions

~5 minutes

~8 minutes

~24 hours

+10 °C

~5 minutes~5 minutes~18 hours

+20 °C

~5 minutes~4 minutes~14 hours

+30 °C

~5 minutes~4 minutes~12 hours+45 °C

1Only for inspection or for application of next layer.

Note: Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Application steps

SUBSTRATE PREPARATION

The surface must be sound, of sufficient strength, clean, dry and free of dirt, oil, grease and other contamination. Depending on the material the substrate must be primed or mechanically cleaned. Grinding may be necessary to level the surface. Suitable substrates are such as: Concrete, bituminous felts and coatings, metal, brickwork, asbestos cement, ceramic tiles.

For detailed information regarding substrate preparation and primer chart please refer to Method Statement No. 850 915 11.

MIXING

Dose and mix with suitable two-component spray equipment. Maintain recommended product and hose temperature.

Recomended pressure:

Component A +  B 160–180 bar.

Ensure equal pressure of component A + B. The accuracy of pressure, mixing and dosage must be controlled regularly with the equipment.

APPLICATION

Prior the application of Sikalastic®-851 R the priming coat if used must have cured tack-free. For the Waiting Time / Overcoating please refer to the PDS of the appropriate primer. Damageable areas (handrails etc.) have to be protected with tape or plastic wrapping.

Waterproofing:

Spray apply Sikalastic®-851 R with suitable two-component hot spray equipment. Possible suppliers of spray equipment are Gama, Graco, Isotherm, WiWa, Reaku etc.

 

UV Protection:

One layer of Sikalastic®-621 or Sikalastic®-445 applied either by roller or airless spray.
 
For more detailed application engineering information pls. refer to the appropriate method statement.

CLEANING OF EQUIPMENT

Clean all tools and application equipment with Thinner C immediately after use. Hardened and/or cured material can only be removed mechanically.