Sikacryl®-112 Universal
Sikacryl®-112 Universal is a 1-part, acrylic, water-based joint sealant for internal joints with low movement and internal crack filling. It is non-sag and over-paintable. It has good adhesion to various construction materials even without a primer. Movement capability ±7,5 %.
- 1-part ready to use
- Good application properties
- Non-sag
- Good adhesion to various substrates
- Movement capability ±7,5 %
- Over-paintable
Usage
Sealing joints for:- Interior joints on many types of substrate with low movement
- Connections around window and door frames
- Around wall and ceiling penetrations
- Internal cracks not exposed to permanent water immersion
Advantages
- 1-part ready to use
- Good application properties
- Non-sag
- Good adhesion to various substrates
- Movement capability ±7,5 %
- Over-paintable
Packaging
280 ml cartridge: 12 cartridges per box
Refer to current price list for packaging variations.
Colour
White
Product Details
APPROVALS / CERTIFICATES
- CE Marking and Declaration of Performance to EN15651-1 - Sealants for non-structural use in joints for facade elements.
Composition
1-part acrylic
Shelf life
18 months from the date of production
Storage conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.
Density
1,60 kg/l | (ISO 1183-1) |
Product declaration
EN15651-1: Sealants for non-structural use in joints for facade elements.
Compatibility
Concrete, aerated concrete, plaster, fibre cement, brick, plasterboard, aluminium, UPVC, wood
Shore A hardness
~50 (after 28 days) | (ISO 868) |
Movement capability
± 7,5 % | (ISO 9046) |
Service temperature
−25 °C to +70 °C (dry)
Joint design
The joint dimensions must be designed to suit the movement capability of the sealant. The joint width must be ≥ 10 mm and ≤ 15 mm. A width to depth ratio of 2:1 must be maintained (for exceptions, see table below).
Typical joint dimensions
Minimum joint width [mm] | Minimum joint depth [mm] |
10 | 10 |
15 | 10 |
Triangular joint profiles must have sides for bonding ≥7 mm.
For larger joints, contact Sika Technical Services for additional information.
Application
Sag flow
< 1 mm (+23 °C) | (ISO 7390) |
Ambient air temperature
+5 °C min./+30 °C max.
Substrate temperature
+5 °C min./+30 °C max. Minimum +3 °C above dew point temperature
Curing rate
~4 mm/24 hours (+23 °C / 50 % r.h.) | (CQP* 049-2) * Sika Corporate Quality Procedure |
Skinning time
~45 minutes (+23 °C / 50 % r.h.) | (CQP 019-1) |
Consumption
Joint length [m] per 280 ml | Joint width [mm] | Joint depth [mm] |
2,8 | 10 | 10 |
1,8 | 15 | 10 |
Consumption calculation formula
Length of joint [m] = 280 ml / (Joint width [mm] x Joint depth [mm])
Litres / Metre run of joint = (Joint width [mm] x joint depth [mm]) / 1000 [m x mm2 / l]
Consumption depends on the roughness and absorbency of the substrate.
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
APPLICATION INSTRUCTIONS
SUBSTRATE PREPARATION
The substrate must be clean, dry, sound and free from oils, grease, dust and loose or friable particles. Sikacryl®-112 Universal adheres without primers and/or activators. For porous substrates, e.g. concrete, plaster and / or wood, Sikacryl®-112 Universal can be dissolved in water (1:1 to 1:5 ratio) and used as a primer if necessary. On plastics and paints, adhesion tests must be carried out prior to application. Iron and steel must be protected with an anti-corrosion primer.
MIXING
1-part ready to use
CLEANING OF EQUIPMENT
Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.