Product Data Sheet Show all documents

Sikalastic®-841 ST

Sikalastic®-841 ST is a two part, elastic, 100% solids, very fast curing and coloured pure polyurea liquid applied membrane with good chemical resistance.

  • Very fast reactivity and curing time
  • Almost immediate return-to-service time
  • Applicable in temperatures from +1°C to +50°C
  • Performs in constant dry temperatures from -30°C to +100°C
  • Excellent crack bridging properties
  • Good chemical resistance
  • Excellent abrasion resistance
  • UV light exposure may lead to yellowing and chalking
  • Not resistant to biogenic sulphuric acid
Product Data Sheet Show all documents

Usage

On concrete
  • Bridge deck Waterproofing membrane
  • Abrasion resistant protective coating in industrial and manufacturing facilities
  • Waterproofing for cut and cover structures
  • Waterproofing for submersed structures
  • Waterproofing on walkways and balconies
  • Waterproofing on floors and car park decks
  • Water retaining structures in power plants
  • Secondary containment structures
  • Tank, bund and pit lining in sewage and waste water treatment plants

Advantages

  • Very fast reactivity and curing time
  • Almost immediate return-to-service time
  • Applicable in temperatures from +1°C to +50°C
  • Performs in constant dry temperatures from -30°C to +100°C
  • Excellent crack bridging properties
  • Good chemical resistance
  • Excellent abrasion resistance
  • UV light exposure may lead to yellowing and chalking
  • Not resistant to biogenic sulphuric acid

Packaging

Part A (Isocyanate)

212 kg drums approx. 189 litres 

Part B (Amine)

191 kg drums approx. 189 litres

Product Details

Sustainability / Certifications / Approvals

SUSTAINABILITY

According USGBC LEED Rating Sikalastic®-841 ST conforms to the requirements of LEED EQ Credit 4.2: Low – Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content < 100g/l

 

APPROVALS / CERTIFICATES

  • Coating for concrete protection according the requirements of EN 1504-2/2004,DoP 02 07 02 05 001 0 000014, certified by FPC Notified Body and provided with CE-Marking
  • Geoscope GmbH, project No. 131303B, 2013, Determination of the durability of the synthetic membrane Sikalastic-841 ST in an autoclave, based on DIN EN ISO 13438
  • BBA/ HAPAS certificate 13/H204 for the use as bridge deck waterproofing membrane according UK standard
  • ETA 033 certificate, No. 13/0653 according ETAG 033
  • KIWA Polymer Institut GmbH, report No. P7074-2, 2013, Testing od static and dynamic crack bridging ability in accordance with DIN EN 1062-7, as well as bond strength after freeze-thaw-cycling with de-icing salt immersion and after thundershower cycling acc. DIN EN 13687-1 and -2, in combination with Sikafloor®-161
  • Truesday Laboraties Inc, certificate for the use in drinking water installations according NSF-ANSI 61, section 6
  • KIWA Polymer Institute GmbH, report No. P7934, 2013, Testing of the root resistance according DIN 4062
Product Information

Composition

pure Polyurea

Shelf life

12 month from date of production

Storage conditions

The packaging must be stored properly in original, unopend and undamaged sealed packaging, in dry conditions at temperatures between +5°C and +30°C. Protected from direct sunlight.

Density

Part A

approx. 1.12 kg/l

Part B

approx. 1.01 kg/l

Density values determined at +20°C

Viscosity

Temperature

Part A

Part B

+20°C

approx. 1200 mPas

approx. 800 mPas

+25°C

approx. 750 mPas

approx. 500 mPas
Technical Information

Shore D Hardness

~45 -  50

(DIN 53505)

Tensile strength

> 15 N/mm²

(DIN 53504)

Crack bridging ability

Class A5

Static

Class B4.2

Dynamic

Application

Application Information

Mixing ratio

Part A : Part B = 1 : 1 volume

Layer thickness

> 2mm

Ambient air temperature

-20°C … +50°C

Relative air humidity

< 85%

Substrate temperature

+1°C … +50°C

≥ 3°C above dew point, beware of condensation

Curing time

24 h / +20°C

Waiting time to overcoating

1 to 2 min / +20°C
Consumption

Consumption

approx. 1.05 kg / m² / mm
Application steps

APPLICATION INSTRUCTIONS

Dose and mix with a suitable air driven or electrical plural component heated spray equipment. Both components must be heated up to +70°C. The accuracy of mixing and dosage must be controlled regularly with the equipment. Thoroughly stir part B (Amine) using a drum stirrer until a homogenous colour is obtained.

CLEANING OF EQUIPMENT

Clean all tools with Thinner C immediately after use. The application equipment has to cleaned and filled with Mesamoll. Hardened and/or cured material can only be removed mechanically.